Inconel 718 pulver is a nickel-chromium alloy powder used primarily in additive manufacturing and metal 3D printing applications. Some key features of Inconel 718 powder include:

• High strength and hardness, including at high temperatures
• Utmärkt korrosions- och oxidationsbeständighet
• God svetsbarhet och maskinbearbetning
• Ability to additively manufacture complex geometries
• Used in aerospace, oil and gas, automotive, and other demanding industries

Inconel 718 is a precipitation hardening nickel alloy with additions of chromium, iron, niobium, molybdenum, titanium and aluminum. It combines corrosion resistance, high strength at elevated temperatures up to 700°C, and ease of fabrication into complex parts using additive manufacturing.

Inconel 718 Powder Composition

The nominal composition of Inconel 718 powder is given below:

The iron content is balanced to 100% by weight. Other trace elements like carbon, manganese and silicon may be present in small quantities.

The key alloying elements in Inconel 718 powder are nickel, chromium, niobium, and molybdenum. Nickel forms the matrix of the alloy providing ductility. Chromium provides oxidation and corrosion resistance. Niobium in combination with nickel and chromium contributes to precipitation hardening. Molybdenum also enhances high temperature strength through solid solution strengthening.

Characteristics and Properties of Inconel 718 Pulver

Inconel 718 powder exhibits the following characteristics:

Mekaniska egenskaper:

• Tensile strength: 1,034 – 1,414 MPa
• Yield strength: 827- 1,103 MPa
• Elongation: Around 20%
• Hardness: 36-48 HRC

Physical Properties:

• Melting point: 1,300°C
• Densitet: 8,19 g/cm3

Thermal Properties:

• Coefficient of thermal expansion: 12.8 x 10^-6 /K
• Maximum service temperature: 700°C
• Thermal conductivity: 11.2 W/m.K

Motståndskraft mot korrosion:

• Excellent corrosion resistance in wide range of acids, alkalis and salts
• Resists sulphidation and oxidation up to 700°C

Partikelstorleksfördelning av Inconel 718-pulver

Typical particle size distributions for Inconel 718 powder for AM processes are:

Narrower particle size distributions like 15-45 μm can be used but generally wider distributions between 15-75 μm are common. Finer atomized powders below 15 μm are also available. Larger particles above 100 μm may need sieving out.

Production Methods of Inconel 718 Powder

The common production methods for Inconel 718 alloy powder include:

• Atomisering av gas – High pressure inert gas (N2 or Ar) disintegrates molten alloy stream into fine droplets which solidify into powder. Provides spherical powder ideal for AM.
• Rotating Electrode Process – Molten material is spun at high speeds in an inert atmosphere to produce flakes or spherical powder. Lower cost than atomization.
• Process med roterande elektrod och plasma (PREP) – Electrodes of Inconel 718 are rotated and melted using a plasma heat source in an inert gas atmosphere. This produces spherical powder suitable for AM.
• Vacuum Induction Melting (VIM) followed by Gas Atomization – Alloy is first melted using VIM to refine composition and remove inclusions. Then atomized into powder.

Gas atomized and plasma rotating electrode powders with controlled particle size distribution are preferred for additive manufacturing with Inconel 718.

Standarder och specifikationer

Inconel 718 powder manufactured for additive manufacturing applications complies with the following specifications:

Chemistry conforms to AMS 5662 and mechanical properties to AMS 5662 or ASTM B214 after built using AM and heat treatment.

Uses and Applications

The major uses and applications of Inconel 718 alloy powder include:

Aerospace: Critical aerospace components like turbines blades, casing, fasteners, gears, waveguides and airframes are additively manufactured using Inconel 718 powder due to its high strength and performance at elevated temperatures.

Olja och gas: Used to print downhole tools, valves, wellhead components that must withstand hydrogen sulfide cracking and corrosion.

Automotive and Racing: Lightweight, high performance components like turbochargers, engine valves and exhaust manifolds are 3D printed in Inconel 718 instead of steel.

Medical and Dental: Surgical instruments, dental crowns and implants printed due to biocompatibility and ability to sterilize through autoclaving.

Tooling: Lightweight Inconel 718 tooling 3D printed using AM offers longer life than traditional tool steels.

Pumps, Valves and Marine Hardware: Components exposed to seawater corrosion and marine environments printed in Inconel 718.

Advantages of Inconel 718 Powder

The advantages of using Inconel 718 powder for additive manufacturing include:

• Parts printed in Inconel 718 can match or exceed the strength levels of forgings
• Ability to produce complex, lightweight geometries not possible with castings
• As-printed surface finish much smoother than machined surfaces
• Lower component weight reduces fuel consumption in aerospace applications
• Excellent corrosion resistance in harsh environments without coatings
• High hardness provides good wear and abrasion resistance
• Fully dense components compared to cast porosity defects
• Reduced lead times and costs compared to forgings or castings

Limitations of Inconel 718 Pulver

Some limitations or disadvantages associated with Inconel 718 powder include:

• High material costs compared to tool steels or aluminum alloys
• Requires hot isostatic pressing (HIP) after AM to achieve best properties
• Difficult to print and process due to poor thermal conductivity
• Prone to cracking and porosity defects without optimized parameters
• Limited number of metal 3D printer models can process Inconel 718 powder
• Post-processing like supports removal, machining and finishing add to costs
• Qualification and certification requires expensive mechanical testing

Kostnadsanalys

Typical pricing for Inconel 718 alloy powder for additive manufacturing is summarized below:

Cost depends on powder particle size distribution, morphology, manufacturing method and purchase quantity. Additional costs are incurred for heat treatment, HIP treatment, machining, testing and certification which can exceed the material cost. Buying fully certified aerospace quality powder will be costlier.

Leverantörer

Some of the major global suppliers of Inconel 718 nickel alloy powder for AM include:

Urvalskriterier

The main selection criteria for Inconel 718 powder includes:

Kemisk sammansättning – Must conform to AMS 5662 or ASTM B214 composition specifications

Fördelning av partikelstorlek – D50 and distribution depends on AM process and desired layer resolution

Pulverform – Highly spherical and smooth powder morphology ensures optimal powder flow and uniform layers

Manufacturing method – Gas atomized and plasma atomized powder preferred over PREP, rotary atomized methods

Föroreningar – Low oxygen and nitrogen levels to prevent defects and cracking issues

Skenbar densitet och tappdensitet – Higher density improves powder reuse rates and packing

Flödeshastighet – Minimum Hall flow rate of 20 sec for 50 g ensures smooth powder spreading

Jämförande analys

Comparison between Inconel 718 powder and alternatives:

Inconel 718 vs Steel Powders

Advantages vs Stainless Steels

• Greater high temperature strength
• Higher hardness and wear resistance
• Improved corrosion resistance

Disadvantages vs Stainless Steels

• Higher material cost
• Lägre duktilitet och brottseghet
• More difficult to print and process

Print Parameters for Inconel 718 Pulver

Typical range of print parameters for Inconel 718 powder on laser powder bed fusion (L-PBF) systems:

Parameters depend on factors like desired resolution, mechanical properties, build rates, OEM printer specifications and powder characteristics.

Post-Processing Operations

The common post-processing steps performed on Inconel 718 printed parts include:

• Powder removal: Excess powder is first blown or brushed off from internal cavities and surfaces
• Stresslindrande: Heating below solutionizing temperature to remove residual stresses
• Varm isostatisk pressning (HIP): Capsule HIP process helps close internal cavities and micropores
• Solution treatment and aging: Precipitation hardening heat treatments to achieve required properties
• Surface machining: CNC machining printed surfaces to lower roughness and bring to tighter tolerances
• Surface conditioning: Glass bead peening, laser polishing or other surface conditioning processes can lower roughness

Vanliga frågor

Why is Inconel 718 the most widely used superalloy for metal 3D printing?

Inconel 718 is popular for additive manufacturing due to its excellent strength at high temperatures, good corrosion resistance, ease of fabrication into complex geometries using 3D printing, ability to perform in extreme environments, and adoption in critical applications in aerospace, oil and gas, etc. where failure is not an option.

Does Inconel 718 require heat treatment after AM?

Yes, heat treatment involving solution annealing and multiple step aging are necessary after printing components in Inconel 718 via AM to adjust the microstructure for transforming into hardened precipitates which provide the excellent mechanical properties.

What is the difference between Inconel 625 vs 718 in additive manufacturing?

The main differences are that Inconel 625 has higher weldability while Inconel 718 offers greater yield and tensile strength. Inconel 718 also performs better under cryogenic conditions while Inconel 625 is preferred for resistance to fatigue, stress corrosion cracking and wear.

Should Inconel 718 parts be HIPed after 3D printing?

Hot isostatic pressing (HIP) helps to eliminate internal voids and microporosity in AM Inconel 718 components. HIP improves ductility, fatigue life and corrosion resistance while reducing potential failure points. Aerospace applications require HIP to ensure highest quality and reliability.

få veta mer om 3D-utskriftsprocesser